AZS Brick ke mofuta oa setene sa li-zirconia-corundum refractory se kopaneng seo e leng mongolo o mokhuts'oanyane oa khutsufatso ea hore AZS ho tsoa ho A ea Al2O3, Z ea ZrO2 le S ea SiO2. Joalo ka No.33 fused cast zirconia-corundum refractory setene se amohela AZS-33# joalo ka khutsufatso ea eona, No.36 fused cast zirconia-corundum refractory setene se amohela AZS-36# joalo ka khutsufatso ea eona le No.41 fused cast zirconia-corundum setene sa refractory se amohela AZS-41 # joalo ka khutsufatso ea eona.
Thepa ea AZS Brick
- Mocheso o Phahameng,
- Khanyetso ea khoholeho ea mobu,
- Thepa e phahameng ea Compactness,
- Thepa e ntle ea Mechini,
- Apara Resistance,
- Alkali corrosion resistance,
- Nako e telele ea tšebeletso.
Sebopeho sa Setene sa AZS
AZS setene sa refractory se nang le 33 ~ 45% ZrO2 content, se sebelisa phofo ea alumina ea indasteri le lehlabathe la zircon le khethiloeng hantle e le lisebelisoa tse tala, tse tšeloang ka hlobo ka mor'a ho qhibiliha ka sebōping sa motlakase o qhibilihisang. ka har'a mohlala oa ente ka mor'a ho qhibiliha ho pholile ha sebōpi sa motlakase le sebopeho sa 'mala o mosoeu, sebopeho sa petrographic se entsoeng ka zirconium corundum le eutectoid ea majoe a tšekaletseng le sebopeho sa karolo ea khalase.
| Sebopeho sa lik'hemik'hale | AZS-33 | AZS-36 | AZS-41 | |
| ZrO2 | ≥33 | ≥35 | ≥40 | |
| SiO2 | ≤16.0 | ≤14 | ≤13.0 | |
| Al2O3 | hanyane | hanyane | hanyane | |
| Na2O | ≤1.5 | ≤1.6 | ≤1.3 | |
| Fe2O3+TiO2 | ≤0.3 | ≤0.3 | ≤0.3 | |
| Thepa ea 'Mele | ||||
| Boima ba bongata(g/cm3): | 3.5-3.6 | 3.75 | 3.9 | |
| Mohatsela o pshatlang Mpa | 350 | 350 | 350 | |
| Mocheso oa ho eketsa mocheso (1000°C) | 0.8 | 0.8 | 0.8 | |
| Mocheso oa exudation. ea mohato oa khalase | 1400 | 1400 | 1400 | |
| Khanyetso ea Corrocion ea ho qhibiliha ha khalase (mm / 24h) | 1.6 | 1.5 | 1.3 | |
| Botenya | PT QX | 3.4 | 3.45 | 3.55 |
Mokhoa oa Tlhahiso oa AZS Brick bakeng sa Glass Furnace
Setene sa AZS se khetha karolo ea 1: 1 ea lehlabathe la zircon le phofo ea alumina ea indasteri, e eketsa palo e fokolang ea NaZO, moemeli oa B20 oa fusion ka mor'a ho kopanya ka ho phethahetseng ka ho qhibiliha le ho tšela hlobo ka mocheso o phahameng oa 1900 ~ 2000 ℃. ka lebaka la hore block ea AZS e na le 33% ZrO2 content. Motheong, nka karolo ea lehlabathe la zircon ea desilicication e le lisebelisoa tse tala ho etsa setene se kopaneng se nang le 36% ~ 41% ZrO2 content.
Tšebeliso ea AZS Brick for Furnace
Setene sa AZS bakeng sa sebōpi se sebelisoa haholo e le lisebelisoa tse thibelang mocheso o phahameng bakeng sa ho hanela ho hlatsuoa ha mocheso o phahameng ka seboping sa tanka ea liindasteri, sebopi sa motlakase sa khalase, indasteri ea tšepe le tšepe, silicate ea sebōpi sa indasteri ea soda. Setene sa mollo sa AZS le sona se ka sebelisoa ka seboping sa tšepe le sets'oants'o sa ho hanela khoholeho ea mobu.