Litene tsa Magnesia li na le lintho tse fetang 90% tsa magnesium oxide mme li nka periclase joalo ka karolo ea mantlha ea kristale. Litene tsa Magnesite li ka aroloa ka mekhahlelo e 'meli ea Litene tse Chesitsoeng tsa Magnesia le Setene sa Chemical Bonded Magnesite. Litene tsa Magnesite li na le ts'ebetso e ntle haholo ea matla a phahameng a mocheso o phahameng oa mocheso le botsitso ba molumo. 'Me e ka sebetsa ka mocheso o phahameng oa 1750 ℃, litene tsa Magnesite ke lihlahisoa tse loketseng bakeng sa kopo ea sebōpi sa khalase.
Thepa ea Magnesia Bricks
- Li-refractorine tse phahameng,
- Ho hanyetsa slag ea alkaline,
- Khanyetso ea khoholeho ea mobu le anti-oxidation e ntle haholo,
- High refractoriness tlas'a mojaro,
- Matla a phahameng a mochini,
- Ho tsitsa ha molumo ka mocheso o phahameng.
Magnesia Bricks Manufacturing Process
Litene tsa Magnesia li ka aroloa ka mefuta e 'meli: setene sa magnesite se chesitsoeng le setene sa magnesite sa lik'hemik'hale. Litene tsa magnesite tse chesitsoeng li entsoe ka thepa e tala ea periclase, ka mor'a ho chesoa ka mocheso o phahameng oa 1550 ~ 1600 ℃ ka ho senya, ho kopanya, ho qhibiliha le ho bopa. Lihlahisoa tse phahameng tsa bohloeki li na le mocheso o chesang o fetang 1750 ℃. Setene sa magnesite se sa chesoang se entsoe ka ho eketsa lik'hemik'hale tse loketseng ka ho qhibiliha, ho bopa le ho omisa.
Lihlopha tsa Litene tsa Magnesia
Ka lebaka la lik'hemik'hale tse fapaneng tsa litene tsa magnesia, tse ka aroloa ka mefuta e sa tšoaneng, 'me litene tsena kaofela li hlahisoa ka sintering. Ho ipapisitsoe le lisebelisoa tse fapaneng tse tala, litene tsa magnesia li ka aroloa ka mekhahlelo e latelang:
Setene sa magnesia se tloaelehileng: lejoe la magnesite le sintered.
Setene sa magnesia se otlolohileng: bohloeki bo phahameng ba sintered magnesite.
Setene sa Forsterite: peridotite
Magnesia calcia brick: Magnesite ea sintered e nang le calcium e ngata.
Setene sa silika sa Magnesia: lejoe le phahameng la silicon sintered magnesite.
Setene sa Magnesia chrome: Magnesite ea sintered le ore ea chrome.
Magnesia alumina setene: sintered magnesite lejoe le Al2O3.
Litlhaloso tsa Litene tsa Rongsheng Refractory Magnesia
| Lintho | Litlhaku tsa 'mele le tsa Lik'hemik'hale | ||||||
| M-98 | M-97A | M-97B | M-95A | M-95B | M-97 | M-89 | |
| MgO % ≥ | 97.5 | 97.0 | 96.5 | 95.0 | 94.5 | 91.0 | 89.0 |
| SiO2 % ≤ | 1.00 | 1.20 | 1.5 | 2.0 | 2.5 | - | - |
| CaO %≤ | - | - | - | 2.0 | 2.0 | 3.0 | 3.0 |
| Ho bonahala Porosity % ≤ | 16 | 16 | 18 | 16 | 18 | 18 | 20 |
| Boima ba Bongata g/cm3 ≥ | 3.0 | 3.0 | 2.95 | 2.90 | 2.85 | ||
| Cold Crushing Matla MPa ≥ | 60 | 60 | 60 | 60 | 50 | ||
| 0.2Mpa Refractoriness Under Load ℃≥ | 1700 | 1700 | 1650 | 1560 | 1500 | ||
| Phetoho e sa feleng ea mola % | 1650℃×2h -0.2~0 | 1650℃×2h -0.3~0 | 1600℃×2h -0.5~0 | 1600℃×2h -0.6~0 | |||
Tšebeliso ea litene tsa Magnesia bakeng sa Sebōpi
Litene tsa Magnesite li loketse mefuta eohle ea libopi tsa mocheso o phahameng, joalo ka libopi tsa metallurgical. Ho phaella moo, litene tsa magnesia li sebelisoa haholo ho lisebelisoa tse ling tse futhumatsang, tse kang hyperthermia tunnel kiln, lesela la sebōpi sa rotary samente, sebōpi se futhumatsang ka tlaase le lerako, kamore e nchafalitsoeng ea sebōpi sa khalase, sebōpi sa mollo oa motlakase tlase le lebota joalo-joalo.
Moetsi oa litene oa Magnesia oa ChinaM
Moetsi oa RS refractory ke moetsi oa litene oa magnesia ea hloahloa Chaena, a ka u fa litene tsa boleng bo holimo tsa magnesite bakeng sa hau. Haeba u na le tlhokahalo ea litene tsa magnesia, kapa u na le lipotso ka litene tsa magnesia mabapi le lipontšo tsa 'mele le lik'hemik'hale, ka kopo ikopanye le rona mahala, thekiso ea rona e tla ikopanya le uena kapele kamoo ho ka khonehang.